ASTM H10Enquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | H10 | ASTM | USA |
Chemical composition%of the ladle analysis of gradeH10
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | V(%) | Cu(%) |
|---|---|---|---|---|---|---|---|---|---|
| 0.35～0.45 | 0.80～1.20 | 0.25～0.70 | ≤0.030 | ≤0.030 | 3.00～3.75 | ≤0.75 | 2.00～3.00 | 0.25～0.75 | ≤0.75 |
Cold pull hardness HBS: 255
Preheat temperature / ℃ : 788
Quenching temperature / ℃ | salt bath furnaces: 1010
Quenching temperature / ℃ | controlled atmosphere furnace: 1024
Holding time/min: 5 to 15
Quenching medium: air cold
Tempering temperature / ℃ : 552
After tempering quartile hardness HRC: 55
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 477(≥) | 163(≥) | 42 | 23 | 21 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 444 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 831(≥) | 636(≥) | 34 | 13 | 22 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 324 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 943 | 485 | 786 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| A 213 S30615 | ASTM | USA | Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes |
| A 240 S30615 | ASTM | USA | Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications |
| A 249 S30615 | ASTM | USA | Welded Austenitic Steel Boiler, Superheater, Heat-Exchanger, and Condenser Tubes |
| A 312 S30615 | ASTM | USA | Seamless, Welded, and Heavily Cold Worked Austenitic Stainless Steel Pipes |
| A 959 S30615 | ASTM | USA | Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels |
| S30615 | ASTM | USA | Austenitic Chromium Nickel Silicon Heat Resisting Steel |
| SA-213 S30615 | ASTM | USA | Specification for Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes |
| SA-240 S30615 | ASTM | USA | Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications |
| SA-249 S30615 | ASTM | USA | Specification for Welded Austenitic Steel Boiler, Superheater, Heat-Exchanger, and Condenser Tubes |
| SA-312 S30615 | ASTM | USA | Specification for Seamless and Welded Austenitic Stainless Steel Pipes |
| A8 | ASTM | USA | Cold-Work Tool Steel |
Enquiry
* Required fields