Home»Grades > Special Alloy > BЖЛ1-BИ
BЖЛ1-BИApplication:Standard vacuum smelting casting high temperature alloy
CategoryTypeSteel gradeStandardCountry
Grades Special Alloy BЖЛ1-BИГОСТRussia

Chemical composition%of the ladle analysis of gradeBЖЛ1-BИ

Si(%)Mn(%)P(%)S(%)B(%)
1.2-2.00.30.020.020.09-0.13
BЖЛ1-BИ
Mechanical properties of gradeBЖЛ1-BИ
Proof strength
Rp0.2(MPa)
Tensile strength
Rm(MPa)
Impact energy
KV(J)
Elongation at fracture
A(%)
Reduction in cross section on fracture
Z(%)
As-Heat-Treated ConditionBrinell hardness(HBW)
345(≥)554(≥)313141Solution and Aging,Annealing,Ausaging,Q+T,etc141
Physical properties of gradeBЖЛ1-BИ
PropertyDensity
kg/dm3
Temperature T
°C/F
Specific heat
J/kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
984(≥)462(≥)334311Solution and Aging,Annealing,Ausaging,Q+T,etc224
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0)N/mm2
Creep rupture strength
(10000h)
(Rp1,0)N/mm2
532989919
BЖЛ1-BИRange of products
Product typeProductsDimensionProcessesDeliver Status
Plates/SheetsPlates/Sheets0.08-200mm(T)*W*LForging,hot rolling and cold rollingAnnealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting
Steel BarRound Bar,Flat Bar,Square BarΦ8-1200mm*LForging,hot rolling and cold rolling,CastBlack,Rough Turning,Shot Blasting,
Coil/StripSteel Coil/Steel Strip0.03-16.0x1200mmCold-Rolled&Hot-RolledAnnealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting
Pipes/TubesSeamless Pipes/Tubes,Welded Pipes/TubesOD:6-219mm x WT:0.5-20.0mmHot extrusion,Cold Drawn,WeldedAnnealed,Solution and Aging,Q+T,ACID-WASHED
Cross Reference Table(Equivalent Grade)
GradeStandardCountryApplication
BЖЛ1-BИГОСТRussia
Russia GOCT Standard vacuum smelting casting high temperature alloy bar
BЖЛ1-BИГОСТRussia
Russia GOCT Standard vacuum smelting casting high temperature alloy bar

Enquiry

Please enter the kg or metric tons.
Please be sure to fill in, in order to contact!
Please be sure to fill in, in order to contact!
Please fill in the Size, Quantity, Weight,, etc...

* Required fields