Location » Home » Grades > Stainless Steels > XH35BTЮ

GOST XH35BTЮ Details

Tags

XH35BTЮ Application:Russia GOCT standard deformation of high temperature alloy grades and chemical composition

Category Type Grade Designations
Grades Stainless Steels XH35BTЮ Russia - GOST ,

Chemical composition(wt.%) of XH35BTЮ grade:

Elements Min.(≥) Max.(≤) Similar Remarks
C - 0.08
Si - 0.60
Mn - 0.60
P - 0.030
S - 0.020
Cr 14.00 16.00
Ni 33.00 37.00
Mo - -
Al 0.70 1.40
Ti 2.40 3.20
Fe - -
W 2.80 3.50
B - 0.020
Russia GOCT standard deformation of high temperature alloy grades and chemical composition

Mechanical properties of grade XH35BTЮ

Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
923 (≥) 325 (≥) 33 41 22 Solution and Aging, Annealing, Ausaging, Q+T,etc 214

Physical properties of grade XH35BTЮ

Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
869 (≥) 674 (≥) 42 42 11 Solution and Aging, Annealing, Ausaging, Q+T,etc 423
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
461 259 268

XH35BTЮ - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
XH35BTЮ GOST Russia
Russia GOCT standard deformation of high temperature alloy grades and chemical composition