CNS SUH36 Details

Tags

SUH36 Application:CNS standard heat resistant steel bar steel grade and chemical composition

Category Type Grade Microstructure Designations
Grades Stainless Steels SUH36 Austenite China - CNS ,

Chemical composition(wt.%) of SUH36 grade:

Elements Min.(≥) Max.(≤) Similar Remarks
C 0.48 0.58
Si - 0.35
Mn 8.00 10.00
P - 0.040
S 0.04 0.09
Cr 20.00 22.00
Ni 3.25 4.50
Mo - -
N 0.35 0.50
CNS standard heat resistant steel bar steel grade and chemical composition

Mechanical properties of grade SUH36

Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
791 (≥) 554 (≥) 23 34 11 Solution and Aging, Annealing, Ausaging, Q+T,etc 342

Physical properties of grade SUH36

Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
998 (≥) 693 (≥) 44 24 11 Solution and Aging, Annealing, Ausaging, Q+T,etc 324
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
228 833 456

SUH36 - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
SUH36 CNS China