ASTM B 670 N07718 Details

B 670 N07718 Application:Precipitation-Hardening Nickel Alloy (UNS N07718) Plate, Sheet, and Strip for High-Temperature Service

Category Type Grade Designations
Grades Superalloys B 670 N07718 USA - ASTM , B 670 (2007) - Precipitation-Hardening Nickel Alloy (UNS N07718) Plate, Sheet, and Strip for High-Temperature Service

Chemical composition(wt.%) of B 670 N07718 grade: B 670 (2007)

Elements Min.(≥) Max.(≤) Similar Remarks
C - 0.03
Cr 17.0 21.0
Mo 2.80 3.30
Ni 50.0 55.0
Al 0.20 0.60
Nb 4.75 5.50
Fe - Bal
Si - 0.35
Mn - 0.35
P - 0.015
S - 0.015
B - 0.006
B 637 N07718

Mechanical properties of grade B 670 N07718 B 670 (2007)

Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
763 (≥) 191 (≥) 21 31 12 Solution and Aging, Annealing, Ausaging, Q+T,etc 324

Physical properties of grade B 670 N07718 B 670 (2007)

Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
474 (≥) 642 (≥) 14 31 44 Solution and Aging, Annealing, Ausaging, Q+T,etc 432
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
565 228 945

B 670 N07718 - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
2.4668 DIN Germany
Classification and designation for superalloys and high temperature intermetallic materials
NiCr19Fe19Nb5Mo3 DIN Germany
Classification and designation for superalloys and high temperature intermetallic materials
A 1014 N07718 ASTM USA
Standard Specification for Precipitation-Hardening Bolting (UNS N07718) for High Temperature Service
B 637 N07718 ASTM USA
Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service
B 670 N07718 ASTM USA
Precipitation-Hardening Nickel Alloy (UNS N07718) Plate, Sheet, and Strip for High-Temperature Service
B 983 N07718 ASTM USA
Precipitation Hardened or Cold Worked, Seamless Nickel Alloy Pipe and Tube
N07718 UNS USA
Ni-Cr Alloy Precipitation Hardenable
Inconel 718 AMS USA
Nickel Alloy, Corrosion and Heat-Resistant, Seamless Tubing 52.5Ni - 19Cr - 3.0Mo - 5.1Cb (Nb) - 0.90Ti - 0.50Al - 18Fe Consumable Electrode Remelted or Vacuum Induction Melted 1775°F (968°C) Solution Heat Treated
Inconel 718 SAE USA
Nickel Alloy, Corrosion and Heat-Resistant, Seamless Tubing 52.5Ni - 19Cr - 3.0Mo - 5.1Cb (Nb) - 0.90Ti - 0.50Al - 18Fe Consumable Electrode Remelted or Vacuum Induction Melted 1775°F (968°C) Solution Heat Treated