Location » Home » Grades > Superalloys > ASTM F75 CoCr Alloy

ASTM ASTM F75 CoCr Alloy Details

Tags

ASTM F75 CoCr Alloy Application:CoCr alloys are widely used within the orthopedics, aerospace, power generation and the dental fields.

Category Type Grade Designations
Grades Superalloys ASTM F75 CoCr Alloy USA - ASTM , ASTM F75-2007 - CoCr alloys are widely used within the orthopedics, aerospace, power generation and the dental fields.

Chemical composition(wt.%) of ASTM F75 CoCr Alloy grade: ASTM F75-2007

Elements Min.(≥) Max.(≤) Similar Remarks
C - 0.35
Si - 0.10
Mn - 1.00
P - 0.02
S - 0.01
Cr 27.00 30.00
Ni - 0.50
Mo 5.00 7.00
W - 0.20
Co - Bal
B - 0.01
Al - 0.10
Ti - 0.1
Fe - 0.75
N - 0.25

Mechanical properties of grade ASTM F75 CoCr Alloy ASTM F75-2007

Yield Strength,Rp 0.2(MPa)

Condition Min Max Similar Note
587 613

Tensile Strength,Rm(MPa)

Condition Min Max Similar Note
1037 1063

Impact,Kv/Ku(J)

Condition Min Max Similar Note

Elongation,A(%)

Condition Min Max Similar Note
17 23

Reduction of area,(%)

Condition Min Max Similar Note
18 22

Hardness

Condition Type Min Max Similar Note

ASTM F75 CoCr is a non-magnetic Cobalt Chrome alloy exhibiting high temperature capability, strength, corrosion resistance, wear resistance as well as excellent biocompatibility.

CoCr alloys are widely used within the orthopedics, aerospace, power generation and the dental fields.


Machining

Parts produced using the Arcam EBM process demonstrate excellent machineability using any conventional machining process.

The F75 built material allow polishing to mirror-like finish for use as articulating surfaces in knee implants or other applications requiring superior surface finish.


Microstructure

Manufacturing CoCr parts with F75 results in fully dense parts without weld lines in the material before or after HIP treatment. The images show the typical microstructure after HIP treatment with different magnification. 

There is no porosity in both the horizontal and vertical cross sections

image.png

Horizontal cross section at 50x and 500x magnification


image.png

Vertical cross section at 50x and 500x magnification





ASTM F75 CoCr Alloy - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
NCF750 KS Korea
Corrosion - resisting and heat - resisting superalloy plates and sheets
NCF751 KS Korea
Corrosion - resisting and heat - resisting superalloy plates and sheets
NCF750 CNS China
CNS Standard heat resistant alloy and corrosion resistant alloy bar and plate type and chemical composition
NCF751 CNS China
CNS Standard heat resistant alloy and corrosion resistant alloy bar and plate type and chemical composition
ASTM F75 CoCr Alloy ASTM USA
CoCr alloys are widely used within the orthopedics, aerospace, power generation and the dental fields.

Enquiry