Location » Home » Grades > Tool Die Steels > T11313

T11313 Enquiry | Print this page

UNS T11313 Details

UNS T11313 Standard Download

Tags

T11313 Application:High-Speed Tool Steel

Category Type Grade Designations
Grades Tool Die Steels T11313 USA - UNS ,

Chemical composition(wt.%) of T11313 grade:

Elements Min.（≥） Max.（≤） Similar Remarks
C 1.00 1.10
Si 0.20 0.45
Mn 0.15 0.40
P - 0.030
S - 0.030
Cr 3.75 4.50
Mo 4.75 6.50
V 2.25 2.75
W 5.00 6.75
Co - -
High-Speed Tool Steel

Mechanical properties of grade T11313

Proof strength
Rp0.2 (MPa)		 Tensile strength
Rm (MPa)		 Impact energy
KV (J)		 Elongation at fracture
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition Brinell hardness (HBW)
597 (≥) 718 (≥) 33 14 23 Solution and Aging, Annealing, Ausaging, Q+T,etc 131

Physical properties of grade T11313

Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm		 Modulus of elasticity
kN/mm2		 Expansion rate
578 (≥) 267 (≥) 22 32 13 Solution and Aging, Annealing, Ausaging, Q+T,etc 422
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2
961 613 112

T11313 - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
T11313 UNS USA
High-Speed Tool Steel

Enquiry