ASTM A7Enquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | A7 | ASTM | USA |
Chemical composition%of the ladle analysis of gradeA7
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Mo(％) | V(%) | W(%) |
|---|---|---|---|---|---|---|---|---|
| 2.00～2.85 | 0.10～0.50 | 0.20～0.80 | ≤0.030 | ≤0.030 | 5.00～5.75 | 0.90～1.40 | 3.90～5.15 | 0.50～1.50 |
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 577(≥) | 886(≥) | 21 | 31 | 24 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 441 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 761(≥) | 178(≥) | 42 | 24 | 22 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 121 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 789 | 648 | 544 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| A 771 S38660 | ASTM | USA | Seamless Austenitic and Martensitic Stainless Steel Tubing for Liquid Metal-Cooled Reactor Core Components |
| A 826 S38660 | ASTM | USA | Seamless Austenitic and Martensitic Stainless Steel Duct Tubes for Liquid Metal-Cooled Reactor Core Components |
| A 831 S38660 | ASTM | USA | Austenitic and Martensitic Stainless Steel Bars, Billets, and Forgings for Liquid Metal Cooled Reactor Core Components |
| S38660 | ASTM | USA | Austenitic Chromium Nickel Molybdenum Stainless Steel-Reactor Grade |
| A7 | ASTM | USA | Cold-Work Tool Steel |
| A723 | ASTM | USA | Heat treatable low alloyed NiCrMo steel |