ASTM T5Enquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | T5 | ASTM | USA |
Chemical composition%of the ladle analysis of gradeT5
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Mo(％) | V(%) | W(%) | Co(%) |
|---|---|---|---|---|---|---|---|---|---|
| 0.75～0.85 | 0.20～0.40 | 0.20～0.40 | ≤0.030 | ≤0.030 | 3.75～5.00 | 0.50～1.25 | 1.80～2.40 | 17.5～19.0 | 7.00～9.50 |
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 895(≥) | 245(≥) | 13 | 22 | 23 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 311 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 811(≥) | 474(≥) | 32 | 23 | 43 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 144 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 835 | 298 | 724 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| Udimet 500 | ASTM | USA | Alloy Castings, Investment, Corrosion and Heat Resistant 53Ni - 18Cr - 18Co - 4.0Mo - 2.9Ti - 2.9Al - 0.006B Vacuum-Melted, Vacuum-Cast, Solution and Precipitation Heat Treated |
| Udimet 500 | ASTM | USA | Alloy Bars, Forgings, and Rings, Corrosion and Heat Resistant 54Ni - 17.5Cr - 16.5Co - 4.0Mo - 2.9Ti - 2.9Al - 0.006B Solution, Stabilization, and Precipitation Heat Treated Consumable Electrode or Vacuum Induction Melted |
| Udimet 500 | ASTM | USA | Alloy Castings, Investment, Corrosion and Heat Resistant 53Ni - 18Cr - 18Co - 4.0Mo - 2.9Ti - 2.9Al - 0.006B Vacuum-Melted, Vacuum-Cast, Solution and Precipitation Heat Treated |
| Udimet 500 | ASTM | USA | Alloy Bars, Forgings, and Rings, Corrosion and Heat Resistant 54Ni - 17.5Cr - 16.5Co - 4.0Mo - 2.9Ti - 2.9Al - 0.006B Solution, Stabilization, and Precipitation Heat Treated Consumable Electrode or Vacuum Induction Melted |
| Udimet 500 | ASTM | USA | Special Purpose Alloys ("Superalloys") |
| T51602 | ASTM | USA | Mold Steel |
| T51603 | ASTM | USA | Mold Steel |
| T51604 | ASTM | USA | Mold Steel |
| T51605 | ASTM | USA | Mold Steel |
| T51606 | ASTM | USA | Mold Steel |
| T51620 | ASTM | USA | Mold Steel |
| T51621 | ASTM | USA | Mold Steel |
| T5 | ASTM | USA | High-Speed Tool Steel |
| Z12CNDV12-03 | ASTM | USA | Iron and steel. Stainless steel for high temperature application |
| Z12CNDV12-03 | ASTM | USA | Iron and steel. Stainless steel for high temperature application |
| Z12CNDV12 Air 9160/C | ASTM | USA | wrought steels used in aeronautical constructions |