Location » Home » Grades > Tool Die Steels > X120Mn12, 1.3401, A128, X110Mn14

EN X120Mn12, 1.3401, A128, X110Mn14 Details

X120Mn12, 1.3401, A128, X110Mn14 Application:X120Mn12, 1.3401, A128, X110Mn14 High-manganese steels with austenitic structure, characterized by high carbon content - on average 1.00-1.20%, and high Manganese content - approx.

Category Type Grade Designations
Grades Tool Die Steels X120Mn12, 1.3401, A128, X110Mn14 European - EN ,

Chemical composition(wt.%) of X120Mn12, 1.3401, A128, X110Mn14 grade:

Elements Min.(≥) Max.(≤)
C 0.90 1.05
Mn 11.00 14.00
Si 0.30 0.90
P - 0.06
S - 0.045

Mechanical properties of grade X120Mn12, 1.3401, A128, X110Mn14

Yield Strength,Rp 0.2(MPa)

Condition Min Max Similar Note
kG/mm2 35 45

Tensile Strength,Rm(MPa)

Condition Min Max Similar Note
kG/mm2 80 110

Impact,Kv/Ku(J)

Condition Min Max Similar Note

Elongation,A(%)

Condition Min Max Similar Note
40

Reduction of area,(%)

Condition Min Max Similar Note
40 45

Hardness

Condition Type Min Max Similar Note
kG/mm2 HB 190 250

Physical properties of grade X120Mn12, 1.3401, A128, X110Mn14

Density, ρ Note
7,71 kg/dm3

Related properties

Heat treatment - To give the characteristic properties to Hadfield steel, the product is subjected to supersaturation at a temperature of 950-1000 ℃ and cooled in water, which gives us austenitic material structure. After this treatment, the steel is difficult to process. By slowly cooling the steel in air from the temperature of about 950 ℃ to room temperature, a mixture of ferrite and manganese cementite appears in the structure.

X120Mn12, 1.3401, A128, X110Mn14 High-manganese steels

Austenitic structure, characterized by high carbon content - on average 1.00-1.20%, and high Manganese content - approx. 12%. 

The ranges of concentration of carbon and manganese depend on the equivalents of the grades of different origin. 

The abrasion-resistant steel grades may differ from the standard, which are also included in the presented table.Surface hardening during grinding and crumbling, good ductility, impact resistance and the ability to withstand dynamic loads are the basic criterion for the selection and use of steel. 

The second essential property is that high-manganese steel, after appropriate heat treatment, is a non-magnetic steel. 

The third and probably the last is the high hardness of the material in the supersaturated state - about 500 HBW.Hadfield abrasion resistant steel strengthens during operation, it is used for elements of equipment and machines that are exposed to abrasion at dynamic and high surface pressures. Unfortunately, it is characterized by very difficult machinability and has low resistance to variable loads.Even the smallest small cracks lead to the formation of fatigue and to the destruction of structural parts during the operation of machinery and equipment.


Similar Steel Grades

110G12, 11 G 12, 110 G 12, X120MN12, X 120 MN 12, 1.3401, 3401, 120 MN 12, HADFIELD, X110MN14, X 110 MN 14, 1.3402, 3402, L120G13, 110G13L, 110Г13Л, G13, Г13, 120G13. 120Г13. EL256. ЭЛ256, X120MN13. X 120 MN 13. AOX 120 MN 13, Z120M12. Z 120 M 12, GD 233, ČSN 17 618, 17618, ČSN 417618, NS 1699, NS1699, BW 10, BW10, MA2, MA3, MA5, MAZ, GX100MN13, 1.3406, 3406, GX120MN13, 1.3802, 3802, GX120MN18, 1.3407, 3407, GX120MNCR13-2, 1.3410, 3410, GX120MN12, G X 120 MN 12, ASTM A128 GRADE A, B2, B3, B4, C


X120Mn12, 1.3401, A128, X110Mn14 - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
X120Mn12, 1.3401, A128, X110Mn14 EN European
X120Mn12, 1.3401, A128, X110Mn14 High-manganese steels with austenitic structure, characterized by high carbon content - on average 1.00-1.20%, and high Manganese content - approx.