AFNOR Z3CND17-11-02 Details
AFNOR Z3CND17-11-02 Standard Download
Z3CND17-11-02 Application:Non alloy and alloy steel bolting for pressure equipement - Specifications
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | Z3CND17-11-02 | France - AFNOR , NF A 35-573 - Stainless steels for general purposes. Plates, wide strips and strips NF A 35-574 - Iron and steel. Stainless steel for general purposes. Semi- finished products, bars and wire rod NF A 36-209 - Iron and steel. Austenitic and austenic-ferritic stainless steels plates for boilers and pressure vessels NF A 49-244 - Steel tubes - Welded austenitic stainless and austenitic ferritic steel rolled tubes for pressure service - Dimensions, technical conditions for delivery NF E 29-043 - Non alloy and alloy steel bolting for pressure equipement - Specifications |
Chemical composition(wt.%) of Z3CND17-11-02 grade: NF A 35-573
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.030 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.040 | ||
| S | - | 0.030 | ||
| Cr | 16.00 | 18.00 | ||
| Mo | 2.00 | 2.50 | ||
| Ni | 10.00 | 12.00 |
Mechanical properties of grade Z3CND17-11-02 NF A 35-573
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 414 (≥) | 814 (≥) | 24 | 44 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 411 |
Physical properties of grade Z3CND17-11-02 NF A 35-573
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 915 (≥) | 796 (≥) | 43 | 31 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 243 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 544 | 586 | 263 |
Z3CND17-11-02 - Form of Supply
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
Cross Reference Table(Equivalent Grade)
| Grade | Standard | Country | Application |
|---|---|---|---|
| 00Cr17Ni14Mo2 | GB | China | Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
| X2CrNiMo18-14-3 | AWS | Germany | Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
| 1.4435 | AWS | Germany | Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
| Z 3 CND 17-11-02 | DIN | France | Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
| TS 60 | SS | International | Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
| Z3CND17-11-02 | AFNOR | France | Non alloy and alloy steel bolting for pressure equipement - Specifications |
| Z3CND17-11-02FF | AFNOR | France | Iron and steel. Stainless steel wire rods for cold forming |