X2CrNiMoN17-11-2 Enquiry | Print this page
ISO X2CrNiMoN17-11-2 Details
ISO X2CrNiMoN17-11-2 Standard Download
X2CrNiMoN17-11-2 Application:Stainless steels - Chemical composition
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | X2CrNiMoN17-11-2 | Austenite | International - ISO , ISO 15510 (2010) - Stainless steels -- Chemical composition ISO 9328-7 (2011) - Steel flat products for pressure purposes - Technical delivery conditions - Part 7: Stainless steels ISO/TS 15510 (2003) - Stainless steels - Chemical composition |
Chemical composition(wt.%) of X2CrNiMoN17-11-2 grade: ISO 15510 (2010)
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.03 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.045 | ||
| S | - | 0.030 | ||
| Cr | 16.00 | 18.00 | ||
| Ni | 10.00 | 12.50 | ||
| Mo | 2.00 | 3.00 | ||
| N | 0.12 | 0.22 |
Mechanical properties of grade X2CrNiMoN17-11-2 ISO 15510 (2010)
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 964 (≥) | 636 (≥) | 41 | 33 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 342 |
Physical properties of grade X2CrNiMoN17-11-2 ISO 15510 (2010)
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 626 (≥) | 169 (≥) | 42 | 41 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 424 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 565 | 944 | 675 |
X2CrNiMoN17-11-2 - Form of Supply
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
Cross Reference Table(Equivalent Grade)
| Grade | Standard | Country | Application |
|---|---|---|---|
| 1.4406 | DIN | Germany | DIN 1654-5 (1989) Cold heading and cold extruding steels; technical delivery conditions for stainless steels; Replaced by DIN EN 10263-5:2002 |
| X2CrNiMoN17-11-2 | DIN | Germany | DIN 1654-5 (1989) Cold heading and cold extruding steels; technical delivery conditions for stainless steels; Replaced by DIN EN 10263-5:2002 |
| X2CrNiMoN17-11-2 | B.S. | UK | Stainless steel bars for pressure purposes |
| 1.4406 | B.S. | UK | Stainless steel bars for pressure purposes |
| X2CrNiMoN17-11-2 | AFNOR | France | Stainless steel bars for pressure purposes |
| 1.4406 | AFNOR | France | Stainless steel bars for pressure purposes |
| X2CrNiMoN17-11-2 | ISO | International | Stainless steels - Chemical composition |